Abstract
The effect of cerium-rich misch metal addition on the microstructure and properties of squeeze cast magnesium alloys AZ81 was empirically investigated. The results indicate that the addition of cerium-rich misch metal modifies the microstructure gradually. With the increase of the RE addition, the amount of Mg 17Al 12 decreases while that of Al 11(RE) 3 increases, accompanied by grain refinement. When the addition reaches 1.5%, the grain refinement becomes obvious. However, when the addition exceeds 2.0%, Al 11(RE) 3 phase coarsens into rod shape and the grain size increases. The tensile properties of the AZ81 at both room temperature and 150°C increase with the addition, and reach their optimal values with the addition of 1.5%. Further increase of the addition to above 2.0% decreases the tensile properties considerably. The tensile fracture of the alloy is characterized by the cleavage of the brittle second phases and ductile dimples of the matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.