AbstractThe present work aimed at the simultaneous improvement in the mechanical and electromagnetic shielding properties of Fe3O4‐carbonaceous/epoxy composites by the reinforcement of two plies of carbon fiber into the epoxy‐filler matrix. In this study, Fe3O4‐activated carbon and Fe3O4‐activated charcoal composites were synthesized by co‐precipitation method and were introduced into the epoxy matrix with different weight percentage (5, 10, and 15 wt%). The BET surface area analysis revealed the high porosity in the Fe3O4‐activated charcoal composite than that of activated carbon composite. The Fe3O4‐activated carbon/epoxy composite showed better mechanical properties than the later. Both the composites showed nearly same EMI SE value. 10 wt% of the filler‐1/epoxy composite showed the highest shielding effectiveness (SE) value of −22.5 dB at 10 GHz whereas 15 wt% Fe3O4@charcoal/epoxy composite showed better SE value of −27.15 dB at 8.8 GHz. The obtained results were supported by the dielectric and magnetic loss tangent studies. The incorporation of carbon fiber enhanced the mechanical property by three times and the EMI SE value by ~15 dB. Thus, the carbon fiber reinforced Fe3O4/carbonaceous epoxy composites may be the potential electromagnetic shielding material for electronics and aircraft industries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.