Abstract
The bearing steel’s high-temperature brittle zone (1250 °C–1100 °C), second brittle zone (1100 °C–950 °C), and low-temperature brittle zone (800 °C–600 °C) were determined by the reduction in area and true fracture toughness. The crack sensitivity was strongest at temperatures of 1200 °C, 1000 °C, and 600 °C, respectively. Various experimental and computational methods were used to establish the phase type, microstructure, size, and mechanical properties of carbides in bearing steel. The critical conditions for crack initiation in the matrix (FCC-Fe, FCC-Fe, and BCC-Fe)/carbides (striped Fe0.875Cr0.125C, netted Fe2.36Cr0.64C, and spherical Fe5.25Cr1.75C3) were also investigated. The values for the high-temperature brittle zone, the second brittle zone, and the low-temperature brittle zone were 13.85 MPa and 8.21 × 10−3, 4.64 MPa and 6.52 × 10−3, and 17.86 MPa and 1.86 × 10−2, respectively. These were calculated using Eshelby’s theory and ABAQUS 2021 version software. The ability of the three carbides to cause crack propagation was measured quantitatively by energy diffusion: M3C > MC > M7C3. This study analyzed the mechanism of carbide precipitation on the formation of high-temperature cracks in bearing steel casting. It also provided the critical conditions for carbide/matrix interface cracks in bearing steel continuous casting, thus providing effective support for improving the quality of bearing steel casting.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.