Abstract
Changing the ratio of carbon to silicon during the epitaxial 4H–SiC growth is expected to alter the dominant deep level trap, which has been attributed to a native defect. The C∕Si ratio was changed from one to six during epitaxial growth of SiC. Diodes fabricated on the epitaxial layer were then characterized using current-voltage and deep level transient spectroscopy. The single peak at 340K (Z1/Z2 peak), was deconvolved into two traps, closely spaced in energy. The concentration of one of the Z1/Z2 traps decreased with increasing C∕Si ratio. This result opposes theoretical predictions of carbon interstitial components, and supports assignment to a silicon antisite or carbon vacancy relationship. The concentration of the second component of the peak at 340K did not depend on the C∕Si ratio, which would indicate an impurity in an interstitial site.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.