Effect of Bracket Base Sandblasting on Bonding of Orthodontic Brackets on Enamel Surface

Abstract

Introduction: In evaluating bond failure, considerable attention has been paid to the various factors that affect bond strength. The bracket–resin interface is the site of usual bond failure. Therefore, many efforts have been accomplished on this interface. The aim of this study was to compare the effects of sandblasting on shear bond strength of three different metal brackets. Materials and Methods: For this experimental study, 180 human maxillary first and second premolars teeth were cleaned and stored in 0.1% thymol solution. The teeth were randomly assigned to either the control ( n = 90) or experimental group ( n = 90). Each group was subdivided into three equal groups ( n = 30). In the control group, three different non-sandblasted metal brackets (American Orthodontics, Dentarum, and 3M Unitek) were bonded with 3M (Unitek) no-mix resin. In the next stage of the experiment, similar brackets were sandblasted and bonded. All samples were pumiced and etched with 37% phosphoric acid for 15 s. The teeth were embedded in blocks of autopolymerization polymethyl methacrylate, utilizing a special device to make their slots parallel to the horizontal. Samples were stored in distilled water for 24 h before testing. Shear bond testing was carried out with UTM Instron machine. Results: Mean shear bond strength of untreated groups was 15.51, 16.60, and 18.58 MPa for American Orthodontics, Dentarum, and 3M Unitek brackets, respectively. Mean shear bond strength of sandblasted brackets was 15.8, 19.36, and 18.66 for American Orthodontics, Dentarum, and 3M Unitek brackets, respectively. Conclusion: This study showed that there was a significant difference in the mean shear bond strength between untreated and sandblasted specimens only in the Dentarum bracket groups.