Abstract
Abstract This paper explores the effect of bond coat processes and surface characteristics on the failure mechanism of thermal barrier coatings (TBC's). TBC's consist of a 300µm thick air plasma sprayed (APS) top coating of ZrO2-8Y2O3 w% and CoNiCrAlY bond coats which were deposited using low pressure plasma spray (LPPS), shrouded air plasma spray (SPAS) and high velocity oxy-fuel (HVOF) combustion spray and different size powder. Bond coat surface profiles were measured by profilometric techniques and surface roughness was calculated according to the measured results. TBC performance and failure mechanisms were evaluated by adhesive bond strength testing, image analysis measurements of porosity, thermal cycling testing. X-ray diffraction and microstructural analyses. Research results show that bond coat deposition processes and surface characteristics had significant effects on the thermal cycling lifetime and failure mechanism.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.