Effect of Blocking and Superconducting Layer Doping on the Superconductivity and Magnetic Properties of Polycrystalline Sr2CaCu2O6

Abstract

The possible difference in the properties upon doping the Sr2CaCu2O6 superconducting or blocking layers with Fe and Eu respectively was investigated in this work. The homogeneous Sr2−yEu y CaCu2O6+δ and Sr2CaCu2−xFe x O6+δ (y = 0, 0.1, 0.5, x = 0, 0.05) compounds were produced by a high-pressure synthesis route. Judging by the magnetic susceptibility measurements, all samples exhibit a superconductivity transition and the Eu/Fe concentration dependencies on the diamagnetic moment and average Tc have been constructed using the experimental data. As a result, an unusual behavior of the Tc value was observed for the samples with doped Eu: a fivefold reduction in the europium concentration in the sample does not give a noticeable effect on the transition temperature value while the diamagnetic signal becomes more stronger. Complex superconducting dome was found for Eu-doped material: 0.1 ≤ y ≤ 0.5 region Tc vs. concentration data were approximated by inverted parabola-like curve with a maximum at y = 0.3. Difference in properties of the Eu and Fe-doped samples was also found in the behavior of the hysteresis loops showed the opposite orientations.