Abstract
This paper reports a bio-based vanillin-derived epoxy (VDE) resin for bio-based natural fiber-reinforced composites. VDE monomer was synthesized, and curing agents, namely, 4,4´-diaminodiphenyl methane (DDM) and isophorone diamine, were used. The prepared VDE resins with various curing parameters were characterized using FTIR, NMR, tensile test, bending test and water contact angle. Further, the interfacial adhesion feasibility of VDE resins on cellulose film was studied through the single-lap shear joint examination and compared with a commercial epoxy, DGEBA. The VDE-DDM resin exhibited excellent interfacial adhesion with cellulose than VDE-IPDA and DGEBA-DDM resins. The cured VDE-DDM thermoset showed a tensile strength of 86.0 ± 6.5 MPa, thermal stability of 241.0 °C at Td5%, and an elastic modulus of 2.9 ± 0.3 GPa, which is better than the commercial epoxy resin. Besides, the developed VDE-DDM resin was used to fabricate treated-jute fiber (TJF)-reinforced composites. The bio-based VDE-DDM/TJF composite's flexural strength was higher than the commercial epoxy resin composite, DGEBA-DDM/TJF. Furthermore, the phosphorus moiety of the VDE-DDM resin endows flame retardancy to the VDE-DDM/TJF composite during combustion. Overall, the appealing properties of bio-based VDE-DDM/TJF composite render environment-friendly and high-performance structural applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Biological Macromolecules
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.