Abstract
Sn-3Ag-3Bi-3In solder has been investigated to improve the understanding of microstructure formation in this solder during solidification and soldering to Cu and Ni substrates. The as-solidified microstructures of Sn-3Ag-3Bi-3In samples were found to consist of a significant fraction of βSn dendrites with a complex eutectic between the dendrites. In total five phases were observed to form during solidification: βSn, Ag3Sn, Bi, ζAg and a “Sn-In-Bi” ternary compound. Soldering of Sn-3Ag-3Bi-3In to substrates changed the phase equilibria in the system and caused the formation of additional phases: Cu6Sn5 during soldering to Cu and Ni3Sn4 and metastable NiSn4 during soldering to Ni. It is shown that metastable NiSn4 forms as a primary phase in a complex 5-component Sn-3Ag-3Bi-3In-Ni system. In and Bi were detected in solid solution in the βSn matrix in amounts of ~1.5-2at% and ~1.2at% respectively. Bi also existed as fine particles of two distinct types. (i): sub-micron (<500nm) coral-like particles and (ii) facetted particles measuring up to 7-8 μm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.