Abstract
Refining effect of B4C nanoparticles in ZL108 alloy on Fe-rich phase was studied in this work. It was observed that B4C nanoparticles apparently refines the size of the Fe-rich phases and partially transforms Fe-rich phases morphology from hollow polyhedron to petal-like shape. The DSC results show that B4C nanoparticles does not affect the initial nucleation temperature of the Fe-rich phase. However, the addition of B4C nanoparticles to ZL108 alloy inhibits the growth of Fe-rich phase. The TEM results confirm that the addition of B4C nanoparticles alters the lattice parameter of Fe-rich phase due to incorporation of C atoms, thereby suppressing the growth of the Fe-rich phase and ultimately leading to its refinement. From the perspective of fracture behavior, the addition of B4C nanoparticles remarkably reduces the stress concentration of Fe-rich phase, and the elongation of the alloy increases by 25.3%. These findings provide a new perspective for further research and development to refine Fe-rich phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.