Abstract
This study provided a fundamental analysis of the viscous behavior and structure of Ti-bearing blast furnace slags modified by different B2O3 additions with a basicity (CaO/SiO2) range of 0.5–0.9. The viscosity of slag melts was measured by rotating cylinder method, and the results showed that both slag viscosity and apparent activation energy for viscous flow remarkably decreased with B2O3 addition. To connect the viscosity variation of slags to the melt structure, Fourier transformation infrared spectroscopy analysis was performed. The results indicated that B2O3 acted as a typical network forming oxide, which was introduced into the network and existed dominantly as a two-dimensional structure, BO3 triangular. With the increase of B2O3 content, the stretching vibration of BO3 triangular gradually became more pronounced, which resulted in a simpler and less complex structure and caused the decrease of slag viscosity.