Abstract
Sintering temperature of the Ba(Zn1/3Ta2/3)O3 (BZT) ceramic is about 1550°C and it decreased to 950°C when B2O3 was added. The BaB4O7 second phase whose melting temperature is 889°C was found in the B2O3 added BZT ceramics. The BaB4O7 second phase assisted the sintering of the BZT ceramics at 950°C. However, the B2O3 added BZT ceramic was not sintered below 950°C and the microwave dielecric properties were not satisfactory. On the other hand, when the B2O3 and the CuO were added, the BZT ceramic was sintered even at 870°C. The BaCu(B2O5) phase which was found in the CuO and B2O3 added BZT ceramics, existed as the liquid phase during the sintering and helped the densification of the BZT ceramics at temperatures lower than 950°C. Good microwave dielectric properties of Q×f=11,000 GHz, εr=26 and τf=0.0 ppm/°C were obtained from the BZT + 5.0 mol% B2O3 + 10.0 mol% CuO ceramic sintered at 870°C for 2 h.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.