Abstract
ObjectiveTo investigate the effect of autoclave induced low-temperature degradation on the adhesion energy between yttria-stabilized zirconia veneered with porcelain. MethodsThe strain energy release rate using a four-point bending stable fracture test was evaluated for two different porcelains [leucite containing (VM9) and glass (Zirox) porcelain] veneered to zirconia. Prior to veneering the zirconia had been subjected to 0 (control), 1, 5, 10 and 20 autoclave cycles. The specimens were manufactured to a total bi-layer dimension of 30mm×8mm×3mm. Subsequent scanning electron microscopy/energy dispersive spectrometry, electron backscatter diffraction and X-ray diffraction analysis were performed to identify the phase transformation and fracture behavior. ResultsThe strain energy release rate for debonding of the VM9 specimens were significantly higher (p<0.05) compared to the Zirox specimens across all test groups. Increasing autoclave cycles lowered the strain energy release rate significantly (p<0.05) from 18.67J/m2 (control) to the lowest of 12.79J/m2 (cycle 10) for only the VM9 specimens. SEM analyses showed predominant cohesive fracture within the porcelain for all cycle groups. XRD analysis of the substrate prior to veneering confirmed a tetragonal to monoclinic phase transformation with increasing the number of autoclave cycles between 5 and 20. The monoclinic phase reverted back to tetragonal phase after undergoing conventional porcelain firing cycles. EBSD data showed significant changes of the grain size distribution between the control and autoclaved specimen (cycle 20). SignificanceIncreasing autoclave cycles only significantly decreased the adhesion of the VM9 layered specimens. In addition, a conventional porcelain firing schedule completely reverted the monoclinic phase back to tetragonal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.