Abstract
ABSTRACTRecently, medium-Mn steels have attracted attention for high-strength automotive components. However, because they exhibit martensitic microstructure at room temperature, low cold roll-ability is concerned so that annealing or tempering is often performed before cold rolling. Therefore, we investigated whether cold roll-ability can be improved by adjusting coiling condition in the hot rolling process. For comparison, some specimens were water-quenched or air-cooled after hot rolling. While the water-quenched specimen revealed cracks at ∼30% cold reduction, air-cooled and coiling-simulated specimens at high reductions above ∼68%. This is because the latter had lower and wider ranged hardness values compared to the former due to partial auto-tempering occurring after coiling. The higher coiling temperature caused higher cold roll-ability probably due to the active recovery of austenite.This paper is part of a Thematic Issue on Medium Manganese Steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.