Abstract
The microstructure, texture, and mechanical properties of the asymmetric welded joint in variable polarity plasma arc (VPPA) welding were studied and discussed in this paper. The asymmetric welded joint was obtained through horizontal welding, where the effect of gravity caused asymmetric material flow. The results showed that the grain size and low angle grain boundary (LAGB) at both sides of the obtained welded joint were asymmetric; the grain size differed by a factor of 1.3. The average grain size of the Base Metal (BM), Lower-weld zone (WZ) and Upper-WZ were 25.73 ± 1.25, 37.87 ± 1.89 and 49.92 ± 2.49 µm, respectively. There is discrepancy between the main textures in both sides of the welded joint. However, the effect of asymmetric metal flow on the weld texture was not significant. The micro-hardness distribution was inhomogeneous, the lowest hardness was observed in regions with larger grain sizes and smaller low angle grain boundary. During tensile strength tests, the specimens fractured at the position with the lowest hardness although it has reached 89.2% of the strength of the BM. Furthermore, the effect of asymmetric metal flow and underlying causes of asymmetric weld properties in VPPA horizontal welding have been discussed and analyzed.
Highlights
Aluminum alloy as a high-performance metal for producing lightweight equipment is widely used in manufacturing industries to promote energy conservation, emission reduction and highly efficient production [1,2]
The effectThe of asymmetric metal flow metal and underlying underlying causes of asymmetric weld properties in horizontal welding have been causes of asymmetric weld properties in Variable Polarity Plasma Arc (VPPA) horizontal welding have been discussed discussed
The effect of asymmetric material flow on the microstructure, texture and mechanical properties of Al welded joint by VPPA welding has been studied in this paper
Summary
Aluminum alloy as a high-performance metal for producing lightweight equipment is widely used in manufacturing industries to promote energy conservation, emission reduction and highly efficient production [1,2]. Welding with advantages of high energy beam and variable polarity gas tungsten arc is known as a “zero-defect” process in the medium thickness welding of Al-alloys [3,4]. VPPA vertical-up welding is the most widely used method: gravity assists material flow into the keyhole pool, producing high-quality welded joints. In non-vertical-up welding gravity will cause asymmetric molten flow [5,6,7], resulting in an asymmetric weld which can weaken the weld quality. Variable position welding is the bottleneck of VPPA Al alloy welding; the flow of molten pool will be asymmetric because of the change of the angle between gravity direction and welding direction, resulting in the asymmetric thermal field distribution, affecting the mechanical properties of welding joints [2,6,7].
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call