Abstract
Apatite wollastonite glass ceramic (AW-GC) (34.2% SiO2, 44.9% CaO, 16.3%P2O5, 4.6% MgO, 0.5% CaF2) was added into a brushite bone cement, which composed of β-tricalcium phosphate (β-Ca3(PO4)2, β-TCP) and monocalcium phosphate monohydrate (Ca (H2PO4)2H2O, MCPM) in powder phases. Cement was prepared using a 3 β-TCP:2 MCPM in weight ratio. To evaluate the effect of AW-GC on the mechanical strength and degradability of brushite bone cement, the powder phases and 1 wt.% of chitosan dissolved in 5 wt.% of citric acid solution were mixed and soaked in simulated body fluid solution at 37 °C for 1, 3, 5,7 and 14 days, respectively. The compressive strength and setting time of AW-GC added in brushite bone cement were studied and compared with pure brushite cement. The pH values increased with addition of AW-GC. Additionally, the obtained brushite bone cements were characterized by XRD, SEM techniques.