Abstract
Magnetic zinc ferrite (ZnFe2O4) nanopowders were synthesized using the sol–gel autocombustion method. X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements demonstrated that thermal decomposition of the 1-mm-thick xerogel layers in air formed monophasic spinel ferrite nanopowders with a particle size less than 30 nm. X-ray photoelectron spectroscopy (XPS) showed that the obtained reaction product contained antisite defects, with zinc ions occurring at the octahedral sites of the spinel structure. The concentration of antisite defects or inversion degree decreased when the relatively low annealing temperature was increased from 150 to 500 °C. Overall, the obtained ZnFe2O4, which is usually antiferromagnetic (exhibits no magnetic moment), demonstrated high saturation magnetization (60.7 emu g−1), and coercive force (56 Oe). This was due to the presence of the antisite defects in the structure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.