Abstract

The effect of annealing treatment on the microstructure of micro arc oxidation (MAO) ceramic film prepared on Al-Mg-Sc alloy was studied. Results suggested that the difference of microstructure of Al-Mg-Sc alloy after various ageing treatment mainly focused on the evolution of dislocation density and the precipitation of β phase (Al3Mg2), and this difference induced the component transformation of surface oxide film from Al2O3 and MgO to MgO and MgAl2O4.Meanwhile, when the other parameters were kept constant, the relevant relations between the microstructure evolution and precipitation phase and the substrate induced the changes of electrical conductivity, then determining the characteristics of MAO ceramic film. Without sacrificing any strength, the optimal MAO ceramic film owning the higher thickness and lower porosity was obtained on Al-Mg-Sc alloy after annealing treatment at room temperature, and tightly bonded to the substrate, which provided a theoretical basis for subsequent research to improve the corrosion resistance of Al-Mg-Sc alloy.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.