Abstract
By DC magnetron sputtering,the Ni films of 600 nm thickness were successfully deposited on BF33 glass substrates.Then annealing at different temperature from 150 to 450°C and different holding time from 3 to 6 hours under vacuum conditions using bonding machine.The surface morphology and structure of Ni films were analyzed by scanning electron microscopy(SEM), films surface roughness and resistivity were investigated by atomic force microscope(AFM) and four-probe tester respectively. The results show that the annealing process contributes to the refinement of the grains.And the films roughness reaches the best level at the annealing temperature of 300 ° C and the roughness data with holding time of 6h is 0.678 nm. Above all,As the annealing temperature increases, the films resistivity decreases significantly.The surface roughness decreases and the resistivity gradually decreases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.