Abstract
The Ni44.1Mn44.2Sn11.7 ribbons were prepared by melt spinning. A single-phase austenite with L21 structure was confirmed in the melt-spun ribbons at room temperature. After the heat treatment, the martensitic transformation temperature increases obviously in the annealed ribbons. This method may be an effective way to tune the characteristic temperatures in the ferromagnetic shape memory alloys. Giant magnetic entropy changes are observed in the annealed ribbons. The peak values at 10kOe are 32.1 and 20.1J∕kgK, for the ribbons annealed at 1123 and 1173K, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.