Abstract

Ga doped ZnO (GZO) thin films were deposited with RF magnetron sputtering on glass substrate and then the effect of post deposition annealing at nitrogen atmosphere on the structural, optical and electrical properties of the films was investigated. The post deposition annealing process was conducted for 30 minutes at different temperature of 150, 300 and , respectively. As increase annealing temperature, GZO films show the increment of the prefer orientation of ZnO (002) diffraction peak in the XRD pattern and the optical transmittance in a visible wave region was also increased, while the electrical sheet resistance was decreased. The figure of merit obtained in this study means that GZO films which vacuum annealed at have the highest optoelectrical performance in this study.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.