Abstract
In this work, Ni(55)Fe(18)Ga(27) ferromagnetic shape memory alloy was prepared through a suck-casting method. The effects of annealing and heating/cooling rate on the martensitic transformation temperatures were investigated by differential scanning calorimetry (DSC). The results showed that the phase transformation temperatures increase with increasing the annealing temperature, upon the heating and cooling process. However, the start and the finish temperatures (M(s) and M(f)) of martensitic phase transformation increased firstly and then decreased upon the cooling process with the increase the annealing time at 300 degrees C. The start and the finish temperatures (A(s) and A(f)) of inverse phase transformation increased slightly upon the heating process with the increase of the annealing time. The results can be explained by the evolution of the microstructure after heat treatment. It was also found that the phase temperatures show great dependence on the heating/cooling rate of the DSC test, A, and At increased and Ms and Mf decreased with the increase of the heating/cooling rate. (C) 2008 Elsevier B.V. All rights reserved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.