Abstract
In order to investigate the early hydration behavior of rapid setting and hardening belite sulfoaluminate cements, the methods of X-ray Diffraction, Scanning Electron Microscope, Compressive Strength test and Setting Times test were used to identify and quantify the hydration kinetics and microstructure of this new-found cements in China. The results showed that the main mineral compositions of high belite sulfoaluminate cement clinker included calcium sulfoaluminate (4CaO·3Al2O3·CaSO4), belite (2CaO·SiO2), ferrite phase, free gypsum and free lime. It was found that not only the setting time and compressive strength but also the composition of hydration products were influenced by anhydrite to some extent. Meanwhile, a mass of AFt and AFm generated along with the hydration process at different ages, overlapped, crossed and penetrated through calcium silicate hydrate gel and aluminum oxide to form a relatively dense structure which could contribute to the high strength of cement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.