Abstract
AbstractIn this study, a blood‐compatible polymer, poly(2‐methoxyethyl acrylate) (PMEA), was grafted onto a gold substrate with various grafting densities (σ) (σ = 0–0.18 chains nm−2), and the amount of hydrated water and mobility of the polymer chain interacting with water molecules were quantitatively evaluated using a quartz crystal microbalance with an admittance system. The amount of hydrated water decreased with increasing σ. By contrast, the mobility of the hydrated PMEA was maximum at σ ≈ 0.12 chains nm−2, revealing that the amount of high‐mobility water at σ = 0.12 was higher than that at other densities. The degree of denaturation of the adsorbed fibrinogen was evaluated based on the hydrodynamic water ratio and viscoelasticity, and was found to increase with increasing σ. The denaturation of adsorbed fibrinogen was suppressed when both the amount of hydrated water and the mobility of hydrated PMEA were high. This study demonstrates that the interfacial state of the polymer chains hydrated in water is important for blood compatibility.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.