Abstract
This work reports on the preparation and characterization of Ti-Al-N thin films deposited by reactive crossed beam pulsed laser deposition (RCBPLD). The elemental composition, vibrational properties and hardness of the deposited films were investigated as a function of the plasma parameters, that is, the Al+ mean kinetic energy and plasma density. The composition of the thin films was determined from X-ray photoelectron spectroscopy (XPS) measurements as well as by Rutherford backscattering spectroscopy (RBS). The structural modifications of the deposited materials due to Al incorporation were characterized by Raman spectroscopy. The hardness of the deposited films was determined by nanoindentation. It was found that by using this experimental configuration the aluminum content in the deposited films was incorporated in a controlled way, from 2.2 to 31.7at.% (XPS measurements), by varying the Al+ mean kinetic energy and the plasma density. Raman results suggest that at low aluminum concentrations a solid solution of Ti(Al, N) is produced, whereas at higher aluminum concentrations a nanocomposite formed of TiAlN and AlN is obtained. Ti-Al-N films with hardnesses up to 28.8GPa, which are suitable for many mechanical applications, were obtained. These results show that the properties of the deposited material are controlled, at least partially, by the aluminum plasma parameters used for thin film growth.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.