Abstract
In this paper, the effect of alumina thickness on Al2O3/InP interface with post deposition annealing (PDA) in the oxygen ambient is studied. Atomic layer deposited (ALD) Al2O3 films with four different thickness values (5 nm, 7 nm, 9 nm, 11 nm) are deposited on InP substrates. The capacitance—voltage (C–V) measurement shows a negative correlation between the alumina thickness and the frequency dispersion. The X-ray photoelectronspectroscopy (XPS) data present significant growth of indium-phosphorus oxide near the Al2O3/InP interface, which indicates serious oxidation of InP during the oxygen annealing. The hysteresis curve shows an optimum thickness of 7 nm after PDA in an oxygen ambient at 500 °C for 10 min. It is demonstrated that both sides of the interface are impacted by oxygen during post deposition annealing. It is suggested that the final state of the interface is of reduced positively charged defects on Al2O3 side and oxidized InP, which degrades the interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.