Abstract
The paper is focused on the influence of alternative fillers on rubber compounds properties. Three different types of powder fillers, drinking water treatment sludge (DWTS), perlite and calcium carbonate, were mixed into rubber compound mixtures. The mixtures were composed of STR20, EPDM, zinc oxide, steric acid, paraffin wax, 2-mercaptobenzothiazole (MBT), sulphur, Wingstay L, and filler. The mixtures were mixed in a Kneader type mixer at temperature of 70°C and then continuously mixed using a two-roll mill at temperature of 70°C. The relationships between type and the amount of filler versus properties of rubber compounds were demonstrated. The results showed that tensile and elongation at break of rubber compounds gradually decreased with increasing the amount of filler. Rubber compounds filled with small particle size filler possessed higher tensile strength and elongation at break than those filled with large particle size filler. Values of DIN abrasion loss of rubber compounds prepared under proper mixing condition were not more than 300 mm3. Under appropriate condition, the rubber compounds with DWTS, perlite and calcium carbonate provided sufficiently high shore A hardness (not less than 50 Shore A hardness). Finally, alternative fillers such as DWTS and perlite were expected to replace calcium carbonate in normal formula.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.