Abstract
The goals of this investigation are the optimization and characterization of Al6061/Al2O3 nanocomposite, which was synthesized by stir casting technique. Different concentrations of Al2O3 nanoparticles as 5, 10, and 15 wt% with an average particle size of 40 nm were examined. The alumina nanoparticles were critically refined and distributed homogeneously in the Al6061 matrix. The microstructure of Al6061/Al2O3 nanocomposite was observed by using scanning electron microscopy. The mechanical properties (tensile, hardness, and ductility) and tribological properties (wear and coefficient of friction) of Al6061/Al2O3 nanocomposites were inspected. The experimental results revealed that there was a significant enhancement in the mechanical properties since it was observed that the yield tensile strength (YTS) increased from 52 to 69 MPa and ultimate tensile strength (UTS) increased from 122 to 158 MPa. The hardness test also showed an enhancement from 28 to 38 BHN at 10 wt% of alumina. The improvement ratios were observed at 32.69%, 29.51%, and 35.71%, respectively. Further, it was found that the incorporation of nano reinforcement can effectively improve the wear rate. It was observed 0.62 × 10-3 (mm3/m) at 40 N of 10 wt% Al2O3 nanoparticles comparison with 1.4 × 10-3 (mm3/m) at the same load of the Al6061 alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.