Abstract
The chemical composition of an AISI type 304 austenitic stainless was systematically modified in order to evaluate the influence of the elements Mo, Ni, Si, S, Cr and Mn on the material’s susceptibility to hydrogen environment embrittlement (HEE). Mechanical properties were evaluated by tensile testing at room temperature in air at ambient pressure and in a 40 MPa hydrogen gas atmosphere. For every chemical composition, the corresponding austenite stability was evaluated by magnetic response measurements and thermodynamic calculations based on the Calphad method. Tensile test results show that yield and tensile strength are negligibly affected by the presence of hydrogen, whereas measurements of elongation to rupture and reduction of area indicate an increasing ductility loss with decreasing austenite stability. Concerning modifications of alloy composition, an increase in Si, Mn and Cr content showed a significant improvement of material’s ductility compared to other alloying elements.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.