Abstract
The stringent conditions are being imposed by the global community to reduce greenhouse gas emissions, will push the search for low carbon footprint alternative binders to ordinary Portland cement. In this pursuit numerous studies have been carried out to synthesize alkali activated concrete (AAC) utilizing industrial by-products, such as, fly ash that is rich in silica and alumina. Natural Pozzolan (NP) is one of such alternative cementitious materials having desirable chemical compositions that could be potentially used to develop AAC. The present work focuses on the effect of curing period, composition of alkaline activators and binder content on the properties of natural pozzolan-based AAC. A total of 15 AAC mixes were prepared by varying the sodium silicate to sodium hydroxide (SS/SH) by weight ratio from 2.0 to 2.75 and binder content between 350kg/m3 and 450kg/m3. Fresh properties, such as, setting time of alkali activated pastes (AAP) and workability of concrete were determined. Compressive strength was measured on the specimens cured for 0.5, 1, 3, 7, 14 and 28days in an oven maintained at 60°C. For selected mixtures, scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques were utilized to study the morphology and mineral composition of the developed alkali activated paste (AAP), respectively. Additionally, FTIR was used to identify functional groups formed in the AAP. The results showed that the composition of alkaline activators and binder content have significant effect on the properties of AAC. Considerable strength gain was recorded after 3days of curing and further curing up to 7days improved the strength. However, continued curing up to 28days marginally decreased the strength. Further, SS/SH ratio of 2.5 and binder content of 400kg/m3, resulting in alkaline activators to binder ratio of 0.525, was found to be suitable for achieving superior strength and microstructural characteristics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.