Abstract
Most Zr conversion coatings are prepared on Al alloys, with Al3+ from the substrate contributing significantly to the film growth process. Thus, the effect of Al3+ on the electrochemical characteristics, surface microstructure and film-formation mechanism of Zr-based conversion coatings on old- rolled steel (CRS) substrates was investigated by growing the coatings with and without Al3+ as an additive. Electrochemical tests indicated that the anticorrosion performance of the Zr-Al coatings prepared in the presence of Al3+ was greatly superior to that of Zr conversion coatings obtained in the absence of Al3+. Field-emission scanning electron microscopy and X-ray photoelectron spectroscopy analysis indicated that adding of Al3+ in the conversion bath changed the surface microstructure of the Zr coating, greatly promoted the deposition of Zr and F on the CRS substrate and increased the film thickness and density. Both coatings were embedded into the etched CRS substrates. The presence of Al3+ additive induced the formation of different coating components. The Zr coating mainly consisted of ZrO2 and some FeFx, whereas the Zr-Al coatings comprised of ZrO2, ZrOxFy, Al2O3, AlFx and some FeFx. The present study results confirm the key role of Al3+ as an additive in the film formation and growth process of Zr coatings and its effect on enhancing the anticorrosion performance of CRS substrates in NaCl solutions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.