Abstract
A columnar Al film was firstly deposited on the top of 7%Y2O3–stabilized zirconia (7YSZ) ceramic coating in thermal barrier coating (TBC) system by magnetron sputtering. A vacuum treatment was then carried out at 700 °C for 1 h and 900 °C for 5 h to improve the erosion resistance of Al-deposited TBC. A α-Al2O3 layer was in situ synthesized on the top of 7YSZ coating via vacuum heat treatment. The microstructure evolution of Al-deposited TBC illustrated that a loose surface-layer and a dense sub-layer formed on the top of 7YSZ coating after vacuum treatment. The phase structures of the as-sprayed TBC and the Al-deposited TBC after vacuum heat treatment were characterized by X-ray diffraction (XRD) and transmission electron microscope (TEM) assisted with focused ion beam (FIB). Particulate erosion resistances of the as-sprayed TBC and treated TBC were compared at room temperature. In addition, erosion mechanism and schematic diagram were proposed. The results show that the Al-deposited TBC after vacuum heat treatment has better particulate erosion resistance than the as-sprayed one.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.