Abstract
The effects of Al content (0.53≤Al≤9.65wt%) on microstructure, texture, magnetic flux density, permeability, core loss and magnetic domain structure of Fe-Al based electrical steel were measured or observed. Average grain size decreased as Al content increased, but Al contents had no severe effects on texture. Magnetic flux density and permeability tends to decrease as Al content increased. Total core loss Ptot was separated into hysteresis loss Ph, eddy-current loss Pe and anomalous loss Pa. As Al increased, Ph increased, but Pe and Pa decreased, so the optimal grain size increased. To reduce core loss of electrical steel with high resistivity, annealing should be conducted at high temperature and for a long time to increase grain size.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.