Effect of aging and testing method on bond strength of CAD/CAM fiber-reinforced composite to dentin

Abstract

ObjectivesTo evaluate and compare the outcomes of shear (S) and microtensile (μT) bond strength tests of CAD/CAM fiber-reinforced composite (FRC) to dentin. Aging with either fatigue or thermocycling were conducted for comparison with baseline microtensile group. MethodsCAD/CAM FRC (Trinia, Bicon LLC, Boston, USA) blocks were milled to 3-mm diameter cylinders for shear and to blocks (5×5×5mm) for μT. Sixty extracted human molars were flattened to obtain dentin surfaces and randomly divided in four groups (n=15): (1) SC: samples tested in shear 24h after bonding; (2) μTC: samples tested in μT 24h after bonding); (3) μTF: samples submitted to mechanical fatigue prior to μT test, and; (4) μTT: thermocycling prior to μT test. Bonding system was applied onto the FRC material (Cera–Resin Bond, CRB, Shofu Dental, Kyoto, Japan). A conventional three-step adhesive system (All-bond 3, Bisco, Schaumburg, USA) was use with a self-cure resin cement (C&B resin cement, Bisco, Schaumburg, USA). Bond strength tests were conducted at 0.75mm/min and data analyzed using Weibull distribution (p<0.05). ResultsWeibull contour plots showed a significantly lower characteristic strength (η) and Weibull modulus (m) for SC (η=6.9MPa and m=1.4) compared to μTC (η=20.9MPa and m=4.5). Fatigued and thermocycled μT groups presented significantly reduced characteristic strength (η=3.1MPa and η=4.1MPa, respectively) compared to μTC. Weibull modulus was significantly reduced only for SC and μTF groups compared μTC. Failure predominantly occurred at the cement/FRC interface. SignificanceFRC bonded to dentin samples presented lower Weibull modulus and characteristic bond strength when immediately tested in shear compared to microtensile. Aging through thermocycling or mechanical fatigue significantly reduced the characteristic strength in microtensile testing, with the majority of failures emerging between restoration material and cement interface.