Abstract
An effect of ageing on mechanical properties of ultrafine grained Al 6061 alloys has been investigated in the present work. The solution treated bulk Al 6061 alloy was subjected to cryorolling to produce ultrafine grain structures and subsequently ageing treatment to improve its both strength and ductility. The hardness and tensile properties of solution treated, cryorolled, cryorolled and aged Al alloys were measured and explained by using their corresponding microstructural morphologies. The pre-cryorolled solid solution treatment combined with post-CR ageing treatment (1300C-30h) has been found to be the optimum processing condition to obtain the ultrafine grained microstructure with improved tensile strength (362MPa) and good tensile ductility (10.7%) in the Al 6061 alloy. The combined effect of precipitation hardening and recovery are responsible for the simultaneous improvement of both strength and ductility observed in the present work.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.