Due to the toxicity of Pb in the soldering alloys, new alloys (lead freeLead free ) are suggested by scholars especially for high-temperatureHigh temperature applicationsApplications . One of the alloys recommended so far is Bi–AgBi-Ag . This alloy has certain similar features to Pb–Sn alloys. Thus, the study focused on several candidate alloys (Bi–1.5–2.5–3.5 wt%Ag) as alternative soldersSolders . In this paper, the mechanical propertiesMechanical properties were studied using shear testShear test . It can be found from the shear testShear test results that increasing the amount of Ag content in the solderSolder matrix positively impact the maximum shear stress and shear strain. The highest maximum shear stress and strain were observed at Bi–3.5 wt%Ag with the value of 13.355 MPa and 44.136 MPa, respectively. Furthermore, the lowest maximum shear stress and strain were observed at Bi–1.5 wt%Ag with the value of 11.032 MPa and 24.955 MPa, respectively. Hence, the fracture behavior shifted from brittle to ductile.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.