Abstract
The effects of additives with Na2S, Na2SO4 and CaSO4 on phase transformation of nickel laterite ore in low-temperature reduction roasting process using carbon monoxide were investigated. The results showed that diffraction peaks of forsterite increased with increasing reduction temperature for 30min with the addition of 10wt% Na2SO4 and 50vol% CO, and diffraction peaks of forsterite increased with increasing the content of Na2SO4 at 900°C for 30min. Comparing the above three additives, phase transformation of nickel laterite ore were strongly influenced with the addition of 10 wt% Na2SO4 and 10 wt% Na2S. Calcium sulphide from the thermal decomposition of CaSO4 was carried out in the reaction product. SEM-EDS analysis result deduced that increasing the dosage of Na2SO4 from 10wt% to 15wt% could promote the polymerization of ferronickel and improve the grade of nickel in ferronickel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.