Abstract

a hehanbinghhb@163.com Abstract. xNi/10NiO-NiFe2O4 cermet and 1BaO-xNi/ (10NiO-NiFe2O4) cermet (x=5,10,17) inert anodes were prepared and their corrosion resistance to Na3AlF6-Al2O3 melts was studied in laboratory electrolysis. The results show that many pores are produced and electrolytes are infiltrated inside inert anodes during electrolysis based on SEM/EDS of anode. The contamination level of nickle, iron and barium in the electrolyte reach steady state after some irregular behaviour early in the tests according to XRF of electrolyte. And the wear rate of 5Ni/(10NiO-NiFe2O4), 10Ni/(10NiO-NiFe2O4), 17Ni/(10NiO-NiFe2O4), 1BaO-5Ni/(10NiO-NiFe2O4), 1BaO-10Ni/ (10NiO-NiFe2O4) and 1BaO-17Ni/ (10NiO-NiFe2O4) is 1.23 cm·year -1 ,1.42 cm·year -1 ,0.96 cm·year -1 ,3.21 cm·year -1 ,2.37 cm·year -1 and 3.94 cm·year -1 , respectively. Thus, sintering agent BaO

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.