Abstract
Al2O3-MgO unfired brick were prepared by using brown corundum, white corundum, fused magnesia and α-A12O3 as main starting materials, Al2O3-SiO2 gel powder as a binder. The effects of Al2O3-SiO2 gel powder on the strength of Al2O3-MgO unfired bricks were investigated. The phase composition was characterized by X-ray diffraction (XRD). The results showed that with an increase of Al2O3-SiO2 gel powder content, room temperature strength first increased and then decreased, and reached an optimum value at 5.5% addition. The hot modulus of rupture continuously increased. This mainly was related to the reactivity of Al2O3-SiO2 gel powder and the formation of mullite at high temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.