Abstract
In this work, Ce was used as the A-site element and three-dimensional ordered macroporous (3DOM) materials as the template to obtain 3DOM CeCo0.7Mn0.3O3 catalyst via excessive impregnation method. The catalyst was subjected to acid/alkali treatment with dilute nitric acid and sodium hydroxide solutions. The results revealed that the catalysts subjected to acid/alkali treatment exhibited better structural and catalytic activity characteristics than the bulk catalyst. Specifically, the specific surface area of the catalyst treated with acid increased from 34.86 to 60.67 m2·g-1, and the relative contents of Oads and Mn4+ species increased. Moreover, the T90% further decreased to 174 °C. As for the catalyst treated with alkali, it exhibited a rougher surface and a wider pore size distribution, producing more lattice defects which were favorable for reaction progress. The T90% was 183 °C, indicating that acid/alkali treatment both had a positive effect on the catalytic oxidation of toluene.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Environmental science and pollution research international
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.