Abstract

The Pb-doped BiSrCaCuO superconducting films were grown by the single source mixed evaporation technique. The microbridges of dimensions 50 mum x 40 mum were fabricated by standard photolithography technologies. Si films with a thickness of 2500 angstrom were deposited on the microbridge area surfaces of BiPbSrCaCuO superconducting films by rf-magnetron sputtering. A greatly lowered zero resistance temperature of the microbridge area of the BiPbSrCaCuO film after Si sputtering was found. A non-linear effect of the current-voltage (I-V) characteristics at 78 K was shown. The high-frequency capacitance-voltage (C-V) curve of this structure at 78 K was symmetrical with the maximum capacitance at V = 0, and the capacitance decreased with increasing applied bias voltage. Afl experimental results are discussed.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.