Abstract
Statement of problem Denture cleansers used in clinical practice can damage resilient denture lining materials. Purpose This study evaluated the effects of a denture cleanser on weight change, roughness, and tensile bond strength on 2 denture resilient lining materials. Material and methods Forty specimens of microwave acrylic resin (Onda-Cryl), 30 mm in diameter and 4 mm thick, were prepared to verify weight change and surface roughness. The specimens were divided into 4 groups consisting of 10 specimens each, relined with a resilient liner (Coe Soft or Dentusoft), and treated (Polident or tap water). To evaluate tensile bond strength, 12 specimens were used for each group. All specimens were stored in artificial saliva for 15 days, immersed once a day in Polident or tap water, and evaluated at 0 hours and after 24 hours and 7 and 15 days. Roughness was evaluated by use of a profilometer. Weight changes were recorded in milligrams and expressed as the percentage of weight difference between the periods of evaluation. Tensile bond strength was determined with a universal testing machine. The specimens were placed under tension until failure by a cross-speed of 5 mm/min with a 500 Kg load cell. The type of failure was determined by use of stereoscopic microscopy at original magnification ×8. The data were submitted to analysis of variance and compared by Tukey’s test (α=.05). Results Specimens immersed in Polident showed higher and significant ( P<.05) weight changes (%) than those immersed in water between 24 hours and 7 days (Coe Soft-Polident: 0.48 ± 0.09; Coe Soft-water: 0.28 ± 0.09; Dentusoft-Polident: 0.44 ± 0.16; Dentusoft-water: 0.22 ± 0.15) and between 7 and 15 days (Coe Soft-Polident: 0.08 ± 0.04; Coe Soft-water: −0.17 ± 0.05; Dentusoft-Polident: 0.01 ± 0.04; Dentusoft-water: − 0.24 ± 0.03). There was significant difference ( P<.05) in roughness (in micrometers), between treatments after 7 days (Coe Soft-water: 4.07 ± 0.22; Coe Soft-Polident: 3.36 ± 0.52; Dentusoft-water: 3.68 ± 0.72; Dentusoft-Polident: 3.26 ± 0.41) and 15 days (Coe Soft-water: 4.88 ± 0.29; Coe Soft-Polident:3.53 ± 0.61; Dentusoft-water: 4.42 ± 1.12; Dentusoft-Polident: 3.68 ± 0.37). Tensile bond strength was highest ( P<.05) after 15 days (Coe Soft-water: 5.19 ± 0.93; Coe Soft-Polident: 4.40 ± 0.38; Dentusoft-water: 4.42 ± 1.15; Dentusoft-Polident: 4.84 ± 1.14). Most failures were cohesive (Coe Soft: 76.04% and Dentusoft: 82.29%). Conclusion Within the limitations of this in vitro study, specimens immersed in Polident demonstrated increased weight changes of resilient liners when compared with tap water, but surface roughness and tensile bond strength were unaffected.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.