Effect of 10% sodium ascorbate hydrogel and delayed bonding on shear bond strength of composite resin and resin-modified glass ionomer to bleached enamel

Abstract

Objective:The aim of this study was to comparatively investigate the neutralizing effect of antioxidant treatment and delayed bonding after bleaching with hydrogen peroxide on the shear bond strength of a composite resin (CR) and resin-modified glass ionomer (RmGI) to enamel.Materials and Methods:Ninety-six freshly extracted human 3rd molars with flat enamel surfaces were divided into six experimental groups (n=12/group) and two control groups (n=12/group). After initial preparation, specimens in Groups 1 and 5 (control groups) were not bleached and the buccal enamel surface of specimens were bonded immediately with CR and RmGI. The samples of the remaining groups were all bleached six hours a day for seven days consecutively. Immediately after bleaching, groups two and six specimens were bonded with CR and RmGI. Groups 3 and 7 specimens were immersed in distilled water at 37°C for 7 days and the specimens in Groups 4 and 8 were treated with 10% sodium ascorbate as an antioxidant agent after bleaching. Specimens in Groups 3 and 4 were bonded with CR and Groups 7 and 8 specimens were bonded with RmGI immediately. After specimens were bonded, the shear bond strength (SBS) was measured. The SBS data analyses were subjected to one-way analysis of variance (ANOVA) followed by Tukey test for comparison of specific mean values.Results:The mean SBS value in Group 2 (immediately bonded with CR after bleaching) was significantly lower than other CR groups (P=0.045). RmGI did not bond to buccal enamel surface of specimens in group 6. There was no significant difference between other groups bonded with RmGI (P>0.05).Conclusions:Applying 10% sodium ascorbate hydrogel and one week delay before bonding resulted in reversal of reduced bond strength of CR and RmGI to bleached enamel.