Abstract
AbstractThe effects of organic montmorillonite (OMMT) on the rheological behaviors and phase morphology of polylactide (PLA) were investigated. The rheological behaviors of nanocomposites showed mainly dependence on both temperature and OMMT content. At low OMMT loading (1 wt %), the complex viscosities showed a Newtonian plateau in low frequency region at low temperatures and converted to a shear‐thinning behaviors with increasing temperature. In comparison, at high OMMT loadings (above 5 wt %), strong shear‐thinning behaviors were observed in the full range of frequencies and temperatures. The results demonstrated rheology of PLA/OMMT is highly sensitive to the nanofillers filled materials. A pseudo‐solid‐like behavior at long scale time in the hybrids with OMMT loading was higher than 5 wt %, this response was related to the formation of a network structure across the polymer matrix due to strong interactions of PLA and OMMT that confined the relaxation process of the macromolecules. X‐ray diffraction and transmission electron microscopy indicated the nanocomposites at low OMMT loading were mainly exfoliated and intercalated nanocomposites were gradually formed with increasing OMMT loading. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.