Abstract
A combination of tensile stress, rheooptical birefringence, and wide-angle X-ray scattering (WAXS) was used to probe the dynamic response of the low-tacticity ether-soluble (ES) fraction of elastomeric polypropylene (ePP) derived from metallocene 2-arylindene hafnium catalyst. The ES fraction has isotactic pentad distribution [mmmm] = 21% and a very low amount of crystallinity (≤2% by differential scanning calorimetry and WAXS). In tensile stretching and step-strain shearing, ES exhibits unusual deformation behavior of crystalline chains preferentially oriented orthogonal relative to the deformation axis. Under deformation, WAXS shows arcing along the meridian axis at a scattering angle 2θ = 16.0° (d = 0.551 ± 0.002 nm) which coincides with one of the characteristic reflections of the β-form, but the higher order reflection for the β-form at 2θ = 21.3° is not observed. The meridional arcing, which signifies crystallization of the low-tacticity fraction of ePP, is also observed when ES is blended with high...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.