Dynamic Recrystallization Nucleation Mechanism and Precipitation Behavior of Homogeneous Al-Zn-Mg-Cu Alloy during Hot Deformation

Abstract

The hot deformation behavior of Al-Zn-Mg-Cu alloy was investigated by flow stress curves in isothermal hot compression experiments with deformation temperatures of 350–450 °C and strain rates of 0.01 s−1 to 1 s−1, and the constitutive equation of homogeneous alloy was obtained. At the same time, the dynamic recrystallization and precipitation behavior during hot deformation and the relationship between them and the Z parameters were studied by using EBSD and TEM. DRV is the main mechanism of dynamic softening. With the decrease in Z parameter, the softening mechanism changes from dynamic recovery to discontinuous dynamic recrystallization or continuous dynamic recrystallization. At a higher Z parameter, the dislocation density and precipitated phase density are also higher because the high dislocation density provides heterogeneous nucleation sites of the precipitated phase. A large number of precipitates in the alloy also inhibit the nucleation and growth of dynamic recrystallization by hindering dislocation movement and grain boundary migration.