Dynamic Nuclear Polarization of Silicon Carbide Micro- and Nanoparticles.

Abstract

Two dominant crystalline phases of silicon carbide (SiC): α-SiC and β-SiC, differing in size and chemical composition, were investigated regarding their potential for dynamic nuclear polarization (DNP). 29Si nuclei in α-SiC micro- and nanoparticles with sizes ranging from 650 nm to 2.2 μm and minimal oxidation were successfully hyperpolarized without the use of free radicals, while β-SiC samples did not display appreciable degrees of polarization under the same polarization conditions. Long T1 relaxation times in α-SiC of up to 1600 s (∼27 min) were recorded for the 29Si nuclei after 1 h of polarization at a temperature of 4 K. Interestingly, these promising α-SiC particles allowed for direct hyperpolarization of both 29Si and 13C nuclei, resulting in comparably strong signal amplifications. Moreover, the T1 relaxation time of 13C nuclei in 750 nm-sized α-SiC particles was over 33 min, which far exceeds T1 times of conventional 13C DNP probes with values in the order of 1–2 min. The present work demonstrates the feasibility of DNP on SiC micro- and nanoparticles and highlights their potential as hyperpolarized magnetic resonance imaging agents.