Abstract
AbstractBoth real and imaginary components of the complex shear viscosity have been determined as a function of strain amplitude, frequency and temperature for various samples of poly(vinyl chloride), PVC, and chlorinated PVC of increasing chlorine content, with the aid of a Rheometrics mechanical spectrometer using eccentric rotating disk geometry. Different methods of sample preparation (low temperature dry‐blending, high temperature extrusion or calendering) were used to study thermomechanical history effects. Results obtained in the region of “linear” viscoelastic behavior were compared with those of capillary flow experiments: at relatively high temperatures the validity of the Cox‐Merz relationship was confirmed. Use of time‐temperature superposition procedures made it possible to predict the important variation of viscosity over a broad range of shear rates. The experimental results in particular with regard to the strong influence of temperature and thermal history, were tentatively interpreted in terms of a supermolecular structure due to the presence of ordered domains (microcrystallites) of variable amount and size. This interpretation was shown to be consistent with differential scanning calorimetry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.