Abstract
The relaxation behavior of six fluorinated aromatic poly( ethers ) was investigated using dynamic mechanical analysis. The glass transition temperature was found to increase as the size and rigidity of linking groups increased and varied between 168°C for a dimethyl linking group and 300°C for a bicyclic benzoate ether-linking group. For the α-relaxation the steepness of time/temperature plots and broadness of the loss curves could be qualitatively correlated with chemical structure in a manner predicted by the coupling model of relaxation. Well-separated sub-T g transitions were also observed, as a shoulder on the low temperature side of the α-peak, and as a broad, low loss transition around -100°C. The higher temperature process was similar to the structural relaxation often found in quenched glassy polymers, while the position, intensity, and breadth of the subambient process was sensitive to chemical structure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.