Abstract
Impact behavior related to crack initiation and growth of cast A357 (Al–7Si–0.7Mg) alloy was experimentally investigated. Dynamic fracture toughness for various artificial aging conditions were evaluated by exploiting instrumented impact Charpy V-notch experiments; impact tests were preferred instead of the standard fracture toughness tests in order to have a fast assessment of the effect of artificial aging on the fracture toughness behavior. Characteristic points of impact load–deflection curves related with cracking were identified and post-correlated with different artificial aging conditions. Absorbed impact energies for stable and unstable crack growth were calculated for 28 different aging conditions; resulting cracking velocity at the unstable crack regime (rebound compliance) was also calculated and it was found that rebound compliance is inversely related to ductility. Cracking initiation load values were identified by exploiting the compliance changing rate method; both stress intensity factor and J-integral analysis were employed to calculate critical dynamic fracture toughness values. They were found to be slightly higher than corresponding quasi-static properties and they are both changing with varying aging conditions. Limitations and results of both notch-fracture toughness analyses were discussed by taking into account the material aging condition. Performed scanning electron microscopy on the fracture surfaces revealed the fracture mechanism that is correlated with respective microstructure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.